Shanghai Bozhong Metal Group Co. Ltd

Model Number: ZXL100 Brand Name: Baosteel, TISCO Key Specifications/Special Features: Description:Nickel hot work tool steel with good harden ability. Uniform hardness over section also at great dimensions. Resistance under impact loadings. Very good strength and toughness. Good tempering resistance and dimensional stability. Tools can be water or air cooledApplications:Forging tools, dies of all sorts, shapes and sizes, hot forging and pressing tools for steel and metal. Moulds, bushings, piercersChemical Composition (in weight%)
C 0.55
Si 0.25
Mn 0.75
Cr 1.10
Mo 0.45
V 0.10
Ni 1.65

Physical properties (average values) at ambient temperature:
Modulus of elasticity [10³ x N/mm²]: 215
Density [g/cm³]: 7.84
Thermal conductivity [W/m.K]: 36.0
Electric resistivity [Ohm mm²/m]: 0.30
Specific heat capacity [J/g.K]: 0.46

Soft annealing:
Heat to 650-700℃, cool slowly in furnace. This will produce a maximum Brinell hardness of 248

Stress relieving:
Stress relieving to remove machining stresses should be carried out by heating to 650℃, holding for one hour at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment

Hardening:
Oil: Harden from a temperature of 830-870℃followed by oil quenching. Hardness after quenching is 58 HRC
Air: Harden from a temperature of 830-900℃followed by oil quenching. Hardness after quenching is 56 HRC

Forging:
Hot forming temperature: 1050-850℃

Machinability:
The machinability rating of D3 is roughly 25% that of free machining carbon steel 1018. Due to its abrasion resistant nature, machining in the hardened condition should be limited to finish grinding

Specifications:
Grade: DIN 56NiCrMoV7
Standard: DIN, GB
Length: 1500-6000mm
Width: 100-1250mm
Thickness: 0.3-200mm
Certification: ISO
Technical treatment: cold-rolled and hot rolled

Packing and delivery:
Packing: standard export seaworthy package or as customers’requirements
Delivery: 7-20 days after received deposit of T/T